EPOX 210 A+B


is a transparent epoxy resin with low viscosity.

Can be used as a casting resin, adhesive or for laminating. Its properties can be adjusted by adding fillers (Filler K5, chalk, aluminium powder or granules, groundglass, mica, graphite, PTFE, pigments, etc.)
             
EPOX 210A+B is a high quality universal binder based on epoxide resin, used primarily for:

-       Binding several materials, mostly metal, wood, stone, marble, concrete, plastic (except 
       PE,PP,PTFE)

-       Making of glass, carbon and kevlar reinforced elements, as automobile or
      aeroplane prototypes, museum replicas, etc.

-       Sealant for tool moulds

-       Making industrial floors

-       Moulding statues, stucco, etc.

-       Used for filling joints in tile, concrete  andnatural stone paving
-       Sealant for fixing elements in electronics

 

ADVANTAGES

High tensile and compressive strength.

Low viscosity enables mixing with high quantities of inert filler, carbonates,talc, metal and ceramic dust.

 

Resistant to water, oil and diluted chemicals.



PROPERTIES

Mixing ratio A:B

2:1 parts by weight

Component viscosity at 25°C

A: 500-900 mPa.s

B: 250 mPa.s

Mixture viscosity after 5 min at 25°C

approx. 600 mPa.s

Pot life of mixture at 20°C:

                quantity 100g

                quantity 200g

 

30 min

11 min

Curing time

depends on the quantity of the binder and the type of filler, from 6 to 24 hours, final strength after 24 hours

 

 

MECHANIC PROPERTIES OF SOLID BINDER

 

 

 

Tensile strength

40 N/mm²

Elongation at break

4-5%

Module of elasticity

2300 N/mm²


Storage: in well sealed original containers at +10 to +25°C

Shelf life:6 months

APPLICATION

MOULDING: Big quantities of Epox 210 harden much more quickly, especially when no fillers are used. MODRIN silicone rubber is recommended for moulding. Modrin is self-separating and does not need a release agent. For all other materials we recommend release agents V or S.

BINDING:First, the surface has to be thoroughly cleaned, dusted and dried. Metal surfaces have to be corrosion free. Roughen the area with a wire brush or sand paper. Acetone, benzine or  trichlorethylene can be used for degreasing unporous surfaces. Do not use solvents for degreasing porous surfaces.Thoroughly mix the glue in bigger packaging before use. Prepare the glue by mixing it in proper ratio. Apply the homogenous mixture to one of the surfaces.Bind them together and if necessary, fixate them. Remove the glue stains while fresh, using one of the above mentioned solvents. Do not dilute the resin!



 



     





  
   


Follow us on:

Facebook
Twitter
Google Plus
Name:
Email:
Message:

Enter the correct result.

3 plus 5 is equal to:
Vse pravice pridržane © 2013 Samson Kamnik d.o.o. | Izdelava spletnih strani in programiranje: Ms3 d.o.o.